In-Situ Observation of Subgrain Evolution during Static Recovery of Cold-Rolled Aluminium
Materials science forum, v 467-470(II), pp 1389-1394
15 Oct 2004
Abstract
A method for in-situ studies of the dynamics of individual embedded subgrains during
recovery is introduced. The method is an extension of 3DXRD principles for studies of grain dynamics in connection with recrystallisation. It is limited to studies of foils with a sample thickness of 10-100 subgrains due to diffraction spot overlap. The volume evolution during recovery (annealing at 300°C for 181 minutes) of nine individual subgrains in a deformed sample (38% cold rolled Aluminium) is presented.
Metrics
11 Record Views
Details
- Title
- In-Situ Observation of Subgrain Evolution during Static Recovery of Cold-Rolled Aluminium
- Creators
- Erik M. Lauridsen - Technical University of DenmarkHenning Friis Poulsen - Technical University of DenmarkC. Gundlach - Technical University of DenmarkR.D. Doherty - :Wolfgang Pantleon - Risø National LaboratoryL. Margulies - Risø National Laboratory
- Publication Details
- Materials science forum, v 467-470(II), pp 1389-1394
- Publisher
- Trans Tech Publications Ltd
- Resource Type
- Journal article
- Language
- English
- Academic Unit
- [Retired Faculty]
- Web of Science ID
- WOS:000225119800216
- Scopus ID
- 2-s2.0-17144362186
- Other Identifier
- 991019167733904721
InCites Highlights
Data related to this publication, from InCites Benchmarking & Analytics tool:
- Collaboration types
- Domestic collaboration
- International collaboration
- Web of Science research areas
- Crystallography
- Materials Science, Multidisciplinary
- Metallurgy & Metallurgical Engineering