Monitoring Damage Accumulation in Filament-Wound Graphite/Epoxy Laminate Coupons During Fatigue Loading Through Acoustic Emission
Journal of reinforced plastics and composites, v 3(1), pp 2-38
Jan 1984
Abstract
Damage accumulation during low cycle tension-tension fatigue loading has been monitored through acoustic emission for filament-wound graphite/epoxy [±24/90/0/ ±45/0/90/±24]
T
laminate coupons. Test frequency was 0.1 and 1.0 Hz at different dynamic load levels and specimens were cycled up to 5,000 and 15,000 cycles at a fatigue load ratio of 0.1. Unnotched and double edge notched specimens (300 × 25 mm in dimensions) were tested, with notch length-to-width ratios of 0.15 and 0.25.
Metrics
5 Record Views
9 citations in Scopus
Details
- Title
- Monitoring Damage Accumulation in Filament-Wound Graphite/Epoxy Laminate Coupons During Fatigue Loading Through Acoustic Emission
- Creators
- Jonathan Awerbuch - Drexel UniversityMadhu Madhukar - Department of Mechanical Engineering and Mechanics Drexel University Philadelphia, Pennsylvania 19104Michael R. Gorman - Testing and Methods Department Hercules Bacchus, Inc. Magna, Utah 84044
- Publication Details
- Journal of reinforced plastics and composites, v 3(1), pp 2-38
- Publisher
- Sage
- Resource Type
- Journal article
- Language
- English
- Academic Unit
- Mechanical Engineering and Mechanics
- Scopus ID
- 2-s2.0-0021161468
- Other Identifier
- 991019296581104721