Poly(acrylic acid)-guided synthesis of helical polyaniline microwires
Polymer (Guilford), v 46(14), pp 5329-5333
2005
Abstract
We present a facile method to prepare helical polyaniline (PANI) microwires or rods guided by poly(acrylic acid) (PAA). The average length and diameter of the helical strands were about 3.5
μm and 500
nm, respectively. The pitch distance was about 400
nm. The morphology of the helical PANI microwires was affected by the concentration of PAA. As the concentration was decreased to below 0.05
mg/ml, helical wire- or rod-like products were observed. The structure of the helical polyaniline microwires were characterized by means of TEM, SEM, XRD, FTIR and UV–vis spectroscopy.
Metrics
Details
- Title
- Poly(acrylic acid)-guided synthesis of helical polyaniline microwires
- Creators
- Xiaofeng Lu - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Youhai Yu - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Liang Chen - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Huaping Mao - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Lifeng Wang - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Wanjin Zhang - Alan G MacDiarmid Institute, Jilin University, Changchun 130012,#N#People’s Republic of China#N#Yen Wei - Drexel UniversityLita W Chen - Pediatrics
- Publication Details
- Polymer (Guilford), v 46(14), pp 5329-5333
- Publisher
- Elsevier
- Resource Type
- Journal article
- Language
- English
- Academic Unit
- Pediatrics
- Web of Science ID
- WOS:000229945500040
- Scopus ID
- 2-s2.0-19944414966
- Other Identifier
- 991019168417004721
InCites Highlights
Data related to this publication, from InCites Benchmarking & Analytics tool:
- Collaboration types
- Domestic collaboration
- International collaboration
- Web of Science research areas
- Polymer Science