Surface characterization of ultrathin atomic layer deposited molybdenum oxide films using high-sensitivity low-energy ion scattering
Journal article   Open access   Peer reviewed

Surface characterization of ultrathin atomic layer deposited molybdenum oxide films using high-sensitivity low-energy ion scattering

Raivathari M. Singhania, Henry Price, Vaneck Y. Kounga, Benjamin Davis, Philipp Bruener, Ryan Thorpe, David J. Hynek, Judy J. Cha and Nicholas C. Strandwitz
Journal of vacuum science & technology. A, Vacuum, surfaces, and films, v 39(6), 063210
01 Dec 2021
DOI: https://doi.org/10.1116/6.0001164
url
https://doi.org/10.1116/6.0001164View
Published, Version of Record (VoR) Restricted

Abstract

Materials Science Materials Science, Coatings & Films Physical Sciences Physics Physics, Applied Science & Technology Technology
Few-layer, high quality, molybdenum oxide films were successfully grown using atomic layer deposition (ALD) and characterized using high-sensitivity low-energy ion scattering (HS-LEIS). The deposition quality, uniformity, and number of layers (thickness) of these films have a drastic effect on overall film properties and, therefore, on performance in electronic devices. In particular, achieving uniform and reproducible nucleation is important for creation of single-monolayer films. However, islanding often occurs during film growth in which film discontinuities or nonuniform thicknesses are formed, both of which are undesirable. We have investigated the uniformity and thickness control of molybdenum oxide films that are deposited via ALD and are precursors to MoTe2 transition metal dichalcogenides. HS-LEIS was used to assess surface coverage and islanding of thin MoOx films ranging in thickness from 0.2 nm to over 7 nm. The absence of a signal from the substrate indicated uniform nucleation and that complete surface coverage by MoOx occurred at a film thickness of approximately 0.6 nm (14 ALD cycles). Monte-Carlo-based simulations were used to predict LEIS spectra, which allowed for quantitative analysis of nucleation and film growth. These simulated spectra of few-layer films further confirmed that the grown films exhibited uniform nucleation. Published under an exclusive license by the AVS

Metrics

16 Record Views
3 citations in Web of Science
3 citations in Scopus

Details

InCites Highlights

Data related to this publication, from InCites Benchmarking & Analytics tool:

Collaboration types
Domestic collaboration
International collaboration
Web of Science research areas
Materials Science, Coatings & Films
Physics, Applied
Logo image