Unimpeded migration of ions in carbon electrodes with bimodal pores at an ultralow temperature of −100 °C (Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ta03988k)
Journal of materials chemistry. A, Materials for energy and sustainability, v 7(27), pp 16339-16346
01 Jan 2019
Featured in Collection : UN Sustainable Development Goals @ Drexel
Abstract
The ability to rapidly charge (and discharge) energy storage devices at extremely low temperature (down to −100 °C) is critical for low-temperature applications such as high altitude exploration and space missions. Electric double-layer supercapacitors (EDLCs) are promising energy storage devices under these conditions. However, it is still a great challenge to obtain EDLCs with both high gravimetric/volumetric capacitance and good rate performance at such low temperatures. We found that, in carbon-based EDLCs, the poor performance at low temperature was mainly caused by the sluggish desolvation of ions at the pore openings and low ion migration within pores. Further, we discovered that there exists a minimum pore opening size for ion adsorption and an effect of pore size on rate performance. These findings enable us to envisage a rational pore structure with a special bimodal distribution of micropores and mesopores. In this work, we successfully synthesized high surface area activated carbon (AC) with a similar structure. Based on this AC, record gravimetric/volumetric capacitance (173 F g−1 and 66 F cm−3 at 10 mV s−1 scan rate) and good rate performance (157 F g−1 and 60 F cm−3 at 100 mV s−1 scan rate) were obtained at a temperature of −100 °C.
Metrics
Details
- Title
- Unimpeded migration of ions in carbon electrodes with bimodal pores at an ultralow temperature of −100 °C (Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ta03988k)
- Creators
- Xi Wang - Changzhou UniversityJiang XuJoselito M RazalNingyi YuanXiaoshuang ZhouXuehang WangJianning DingSi QinShanhai GeYury Gogotsi
- Publication Details
- Journal of materials chemistry. A, Materials for energy and sustainability, v 7(27), pp 16339-16346
- Publisher
- Royal Society of Chemistry; Cambridge
- Resource Type
- Journal article
- Language
- English
- Academic Unit
- Materials Science and Engineering; A.J. Drexel Nanomaterials Institute
- Web of Science ID
- WOS:000475689800025
- Scopus ID
- 2-s2.0-85068766374
- Other Identifier
- 991014970043304721
UN Sustainable Development Goals (SDGs)
This publication has contributed to the advancement of the following goals:
InCites Highlights
Data related to this publication, from InCites Benchmarking & Analytics tool:
- Collaboration types
- Domestic collaboration
- International collaboration
- Web of Science research areas
- Chemistry, Physical
- Energy & Fuels
- Materials Science, Multidisciplinary